MILD STEEL GENERAL PURPOSE STICK ELECTRODES
 
BRAND NAME CLASSIFICATIONS APPROVAL REDRYING POLARITY WELDING PRODUCT DESCRIPTION POSITION
SUPERBOND
AWS A/SFA 5.1 E6013
IS 814 ER4212X
ABS, DNV, LRS
TOYO, BV, IRS
NR*
 
AC OR DC(+)
F/H/V-DOWN/
V-up/OH
For welding of STRUCTURAL steels. Deposits smooth & shiny beads with fine ripples.
SUPERBOND-S
AWS A/SFA 5.1 E6013
IS 814 ER4212X
BS 639 E4333R22
DIN 1913 E4333R322
ABS, DNV, LRS
TOYO, BV, IRS
100-110ºC
FOR 1/2 Hr.
AC or DC(+)
F/H/V-DOWN/
V-up/OH
For welding of STRUCTURAL steels, where BEAD FINISH is required. Best suited for VERTICAL UPWARD and OVERHEAD positions.
SUPERBOND-SS
AWS A/SFA 5.1 E6013
IS 814 ERR4222XE
BS 639 E4322RR21
DIN 1913 4322RR622
ABS, DNV, LRS
TOYO, BV, IRS
100-110ºC
FOR 1/2 Hr.
AC or DC(+)
F/H
 
For weilding of STRUCTURAL steels, where HIGH WELDING SPEED is desirable. Best suited for VERTICAL UPWARD and OVERHEAD positions.
             
             
             
 
Notes: Weld metal shall be of radiographic quality.
 
MILD STEEL STICK ELECTRODES (SPECIAL)
 
BRAND NAME CLASSIFICATIONS APPROVAL REDRYING POLARITY WELDING PRODUCT DESCRIPTION POSITION
SUPABASE*
AWS A/SFA 5.1 E7018
   
IS 814 ER4212X
   
DIN 1913 E5144B1026
ABS, BV, DNV, IRS, LRS
GL, NPCIL, IBR, TOYO
RDSO, BIS
250ºC
FOR 1/2 Hr
AC or DC(+)
F/H/V-DOWN/
V-up/OH
For weilding of Mild steel, Medium Carbon steel heavy joints under restrints and subject to dynamic loading. Deposition efficiency 115%
SUPABASE- X X PLUS*
AWS A/SFA 5.1 E7018
   
IS 814 ER4212X
   
DIN 1913 E5144B1026
   
ABS, BV, DNV, IRS, LRS
GL, NPCIL, IBR, TOYO
RDSO, BIS
250ºC
FOR 1/2 Hr
AC or DC(+)
F/H/V-DOWN/
V-up/OH
For weilding of Mild steel, Medium Carbon steel heavy joints under restraints and subject to dynamic loading. Best suited for 5G & 6G positions. Deposition efficiency 115%.
SILOX-Fe
IS 814 ER4122
DIN 1913 E4400A525
   
   
  NR* AC or DC(-)
F/H/V-DOWN/
V-up/OH
For weld deposit of VERY LOW SILICON CONTENT and almost PURE IRON. Weld metal is made CORROSION RESISTANT by molten Zinc. Deposits smooth and shiny beads Recommended for weilding and repairing of hot dip galvanising bath, resurfacing worn-out parts. Also used as sandwitched layer between CS and SS.
TOPSTAR 110
AWS A/SFA 5.1 E7014
IS 814 ERR5222XJ
BS 639 E4322R11011
DIN 1913 E4322RR1115
 
150ºC
FOR 1 Hrs
AC or DC(-) F/H/V-Down For HIGH-PRODUCTIVITY during welding of STRUCTURAL STEEL.Best suited for VERTICAL & DOWN HAND positions. Deposition efficiency 110%.
TOPSTAR 140
AWS A/SFA 5.1 E7024
IS 814 ERR5224XK
BS 639 E5122R14032
DIN 1913 ES122RR1135140
 
150ºC
FOR 1 Hrs
AC or DC(-) F/H For HIGH-PRODUCTIVITY during welding of STRUCTURAL STEEL.Best suited for DOWN HAND & HORIZONTAL positions. Deposition efficiency 140%.
TOPSTAR 210
AWS A/SFA 5.1 E7024
IS 814 ERR5242XL
BS 639 E5122RR21032
DIN 1913 ES122RR1135140
 
150ºC
FOR 1 Hrs
AC or DC(-) F/H For VERY HIGH PRODUCTIVITY during welding of HEAVY STRUCTURES. Best suited for DOWN HAND & HORIZONTAL positions. Deposition efficiency 210%.
TOPSTAR DP
AWS A/SFA 5.1 E7024
IS 814 ERR5242XL
BS 639 E5122RR21032
DIN 1913 ES122RR1135200
 
150ºC
FOR 1 Hrs
AC or DC(-) F/H For DEEP PENTRATION during welding butt and fillet joints. CONCENTRATED SPRAY TYPE ARC. AVOID BEVELLING of joint upto 7mm. Deposition efficiency 102%.
TENALLOY Z PLUS*
AWS A/SFA
5.1		 E7018-1
IS 814 EB5629H3JX
   
BS 639 E5156B11029(H)
   
DIN 1913 E5155B1029
ABS, BV, DNV,GL,
IRS, LRS, NPCIL
IBR, TOYO, RDSO,
BIS
At 300ºC
FOR 2 Hrs
AC or DC(+)
F/H/V-DOWN/
V-up/OH
For Heavy sections and restrained joints in LOW ALLOY STEELS. Excellent TOUGHNESS down to MINUS 50ºC. Recommended for POSITIONAL PIPE WELDING. Deposition efficiency 110%.
TENALLOY R*
AWS A/SFA
5.1		 E7018-G
IS 814 EB5629H3JX
BS 639 E5156B11029(H)
DIN 1913 E5155B1029
 
At 300ºC
FOR 1 Hrs
AC or DC(+)
F/H/V-DOWN/
V-up/OH
For heavy sections and restrained joints in LOW ALLOY STEELS, containing Ni upto 1.0% SUB ZERO TEMP. applications. Deposition efficiency 110%.
TENALLOY R (SPECIAL)*
AWS A/SFA
5.1		 E7018-1
IS 814 EB5629H3JX
BS 639 E5156B11029(H)
DIN 1913 E5155B1029
LRS, ABS, BV
At 300ºC
FOR 1 Hrs
AC or DC(+)
F/H/V-DOWN/
V-up/OH
For heavy sections and restrained joints in LOW ALLOY STEELS, containing Ni upto 1.0%. SUB ZERO TEMP. applications. Deposition efficiency 110%.